牌号简介 About |
---|
Amodel AS -1566 HS树脂是一种65%玻纤和矿物纤维增强聚邻苯二甲酰胺(PPA)树脂,具有较高的变形温度和较高的抗弯模量。该牌号专门开发用于要求高刚度、良好的尺寸稳定性和耐化学性的、具有高成本效益的产品。 Amodel AS -1566 HS树脂常规用途包括电连接器及外壳、汽车零部件、活塞、罩盖、发动机零件及传动部件。 - 黑色: AS-1566 HS BK 324 黑色:AS-1566 HS BK 545 本色:AS-1566 HS NT Amodel® AS-1566 HS resin is a 65% glass and mineral reinforced polyphthalamide (PPA) resin that exhibits a high deflection temperature and high flexural modulus. This grade was designed specifically to be cost effective for most applications requiring high stiffness, good dimensional stability and chemical resistance. Typical applications for Amodel® AS-1566 HS resin include electrical connectors and housings, motor components, pistons, covers, engine parts and transmission components. Black: AS-1566 HS BK 324 Black: AS-1566 HS BK 545 Natural: AS-1566 HS NT |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.84 | g/cm³ | ISO 1183/A |
收缩率 Shrinkage rate |
|||
TD TD |
0.50 | % | ASTM D955 |
MD MD |
0.30 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.10 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
20000 | MPa | ASTM D638 |
拉伸模量 Tensile modulus |
ISO 527-2 | ||
23℃ 23℃ |
MPa | ISO 527-2 | |
100℃ 100℃ |
MPa | ISO 527-2 | |
150℃ 150℃ |
MPa | ISO 527-2 | |
175℃ 175℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
ISO 527-2 | ||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
断裂,24℃ Fracture, 24 ℃ |
MPa | ISO 527-2 | |
断裂,150℃ Fracture, 150 ℃ |
MPa | ISO 527-2 | |
断裂,175℃ Fracture, 175 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
ISO 527-2 | ||
断裂 fracture |
% | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
断裂,24℃ Fracture, 24 ℃ |
% | ISO 527-2 | |
断裂,150℃ Fracture, 150 ℃ |
% | ISO 527-2 | |
断裂,175℃ Fracture, 175 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
ISO 178 | ||
23℃ 23℃ |
MPa | ISO 178 | |
100℃ 100℃ |
MPa | ISO 178 | |
150℃ 150℃ |
MPa | ISO 178 | |
175℃ 175℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
屈服 yield |
MPa | ASTM D790 | |
弯曲强度 bending strength |
ISO 178 | ||
23℃ 23℃ |
MPa | ISO 178 | |
100℃ 100℃ |
MPa | ISO 178 | |
150℃ 150℃ |
MPa | ISO 178 | |
175℃ 175℃ |
MPa | ISO 178 | |
剪切强度 shear strength |
MPa | ASTM D732 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
ASTM E831 | ||
0 到 100℃ 0 to 100 ℃ |
cm/cm/℃ | ASTM E831 | |
100 到 200℃ 100 to 200 ℃ |
cm/cm/℃ | ASTM E831 | |
MD MD |
ASTM E831 | ||
0 到 100℃ 0 to 100 ℃ |
cm/cm/℃ | ASTM E831 | |
100 到 200℃ 100 to 200 ℃ |
cm/cm/℃ | ASTM E831 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
赢创投资新加坡初创公司Revivo BioSystems
2021-12-05 搜料网资讯: 赢创 投资了初创公司Revivo BioSyste ms ,以支持一项技术的开发和商业化,该技术使用真实的4D人体皮肤模型来测试化学、化妆品和药物化合物。这家新加坡初创公司的技术提 |
赢创投资新加坡初创公司Revivo BioSystems 搜料网资讯:赢创投资了初创公司Revivo BioSystems,以支持一项技术的开发和商业化,该技术使用真实的4D人体皮肤模型来测试化学、化妆品和药物化合物。这家新加坡初创公司的技术提供了一种替代动物试验的方法,该方法也更快、更可靠且具有成本效益。 “我们的目标是支持超越当今研究方式的新兴技术,并加速更具可持续性和道德规范的实践,”赢创风险投资负责人伯恩哈德·莫尔 (Bernhard Mohr) 表示。 Revivo的器官芯片系统模拟人体皮肤与被测物质的相互作用。在实验室或人体皮肤样本中生长的皮肤组织被放置在提供营养和试剂的生物芯片上。通过这种方式,该技术为组织模型创造了一个微环境,再现了皮肤的结构和功能。例如,与其他模型系统相比,它模拟血流的功能,允许分析化合物对皮肤组织的局部和全身影响。因此,该平台创建了一个更真实的测量,例如护理产品和皮肤的相互作用。 除了在现实条件下进行测试外,该公司的系统还使测试和采样程序自动化。这提供了一种经济有效的方式来进行新物质监管批准程序中所需的筛选。 “我们对Revivo的投资将消费者安全放在首位,同时不影响动物福利,”赢创护理解决方案业务线负责人Yann d'Hervé 说。“有了这种动物试验的替代方案,我们很自豪能够巩固我们作为可持续专业值得信赖的合作伙伴的地位。” 许多消费者更喜欢未经动物测试的物质,法规也随之效仿。包括澳大利亚、印度、以色列、土耳其和英国在内的40多个国家已通过法律限制或禁止化妆品动物试验。欧盟自2004年起禁止在动物身上进行化妆品试验,自2016年起禁止使用动物数据。在其他国家进行的测试不允许用于审批流程。化学品和药物也正在寻找动物试验的替代品。 赢创已经在其位于新加坡的能力中心参与了无动物生物材料和细胞培养组件的研究。该项目源自于2021年3月成功完成的组织工程项目房。其中,该项目房致力于再生医学领域的组织人工生产。与Revivo的合作符合赢创在能力中心开展创新活动的战略。 Revivo是新加坡公共部门研发机构A*Star(科学、技术和研究机构)的衍生产品。联合投资者是SGInnovate,一家由新加坡政府支持的Deep Tech生态系统建设者和投资者。 “我们期待与赢创一起在我们公司的发展中迈出又一步,”创始人兼首席执行官马西莫·阿尔贝蒂 (Massimo Alberti) 说,他也是Revivo技术的共同发明者和开发者。“这笔新融资将用于发展我们的服务业务并使我们的平台和产品商业化。” Revivo BioSystems是赢创在新加坡的第一笔直接投资。这家德国公司于2018年在上海设立了风险投资办公室,帮助该公司进入亚洲快速扩张的创新创业生态系统。赢创风险投资帮助赢创获得颠覆性技术和创新商业模式以及支持数字化转型。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。