牌号简介 About |
---|
Amodel AS- 4133 HS是33%玻纤增强、润滑、热稳定型聚邻苯二甲酰胺(PPA ),可快速加工、在水温模具中成型。常规应用包括电气和电子元件,尤其是汽车系统用电子电气元件。 - 黑色:AS-4133 HS BK 324 本色: AS-4133 HS NT Amodel® AS-4133 HS is a 33% glass reinforced, lubricated, heat stabilized grade of polyphthalamide (PPA) that offers fast cycle times and moldability in hot water molds. Testing conducted on samples dry as molded and samples conditioned to 50% relative humidity in accordance with ISO-1110, Accelerated Method. Typical applications include electrical and electronic components especially for automotive systems. Black: AS-4133 HS BK 324 Natural: AS-4133 HS NT |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.45 | g/cm³ | ISO 1183/A |
收缩率 Shrinkage rate |
|||
TD TD |
1.0 | % | ASTM D955 |
MD MD |
0.50 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.29 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
11700 | MPa | ASTM D638 |
拉伸模量 Tensile modulus |
ISO 527-2 | ||
23℃ 23℃ |
MPa | ISO 527-2 | |
100℃ 100℃ |
MPa | ISO 527-2 | |
150℃ 150℃ |
MPa | ISO 527-2 | |
175℃ 175℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
ISO 527-2 | ||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
断裂,24℃ Fracture, 24 ℃ |
MPa | ISO 527-2 | |
断裂,150℃ Fracture, 150 ℃ |
MPa | ISO 527-2 | |
断裂,175℃ Fracture, 175 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
ISO 527-2 | ||
断裂 fracture |
% | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
断裂,24℃ Fracture, 24 ℃ |
% | ISO 527-2 | |
断裂,150℃ Fracture, 150 ℃ |
% | ISO 527-2 | |
断裂,175℃ Fracture, 175 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
ISO 178 | ||
23℃ 23℃ |
MPa | ISO 178 | |
100℃ 100℃ |
MPa | ISO 178 | |
150℃ 150℃ |
MPa | ISO 178 | |
175℃ 175℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
弯曲强度 bending strength |
ISO 178 | ||
23℃ 23℃ |
MPa | ISO 178 | |
100℃ 100℃ |
MPa | ISO 178 | |
150℃ 150℃ |
MPa | ISO 178 | |
175℃ 175℃ |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
剪切强度 shear strength |
MPa | ASTM D732 | |
泊松比 Poisson's ratio |
ASTM E132 | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火,3.2 mm 1.8 MPa, annealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,退火,3.2 mm 0.45 MPa, annealed, 3.2 mm |
℃ | ASTM D648 | |
连续使用温度 Continuous use temperature 2 |
℃ | ASTM D3045 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
熔融温度 Melting temperature |
℃ | ASTM D570 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
ASTM E831 | ||
0 到 100℃ 0 to 100 ℃ |
cm/cm/℃ | ASTM E831 | |
100 到 200℃ 100 to 200 ℃ |
cm/cm/℃ | ASTM E831 | |
MD MD |
ASTM E831 | ||
0 到 100℃ 0 to 100 ℃ |
cm/cm/℃ | ASTM E831 | |
100 到 200℃ 100 to 200 ℃ |
cm/cm/℃ | ASTM E831 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
1.6 mm 1.6 mm |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | UL 746 | |
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
mm/min | UL 746 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level 3 |
|||
3.20 mm 3.20 mm |
UL 94 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
透光率 Transmittance 4 |
ASTM D1003 | ||
1070 nm,1.60 mm 1070 nm,1.60 mm |
% | ASTM D1003 | |
1.60 mm,940 nm 1.60 mm,940 nm |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 1500小时 |
3 这些可燃性等级不代表这些材料或任何其他材料在实际着火灾情况下的危险性。 |
4 透光率,自然色牌号 |
【新闻资讯】查看全部
欧盟发布双酚A管控新规
2018-03-23 2018年2月14日,欧盟发布新法规(EU)2018/213,规定了食品接触用清漆、涂料中双酚A的要求,同时修订了(EU)No10/2011中双酚A的限量值,并引入符合性声明的要求。新规直接适用于所有欧盟成员国,将于2018年9月6日开始实施。在此之前,合法投放市场的清漆涂覆或含涂层材料的物品以及塑料材料及物品仍可在市场上销售,直到库存用完为止。 此次新规的主要内容为:一是食品接触清漆或涂料中双酚A迁移量不得超过0.05mg/kg,并且供婴幼儿使用的食品接触清漆或涂料中不得 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |